PET Film(Packaging application)

FP01 12MIC

PROPERTY METRIC(S.I.)UNITS TEST METHOD UNIT TYPICAL VALUE AVERAGE THICKNESS ㎛ 12   YIELD m²/ kg 59.5   TENSILE STRENGTH MD TD kg / ㎟ kg / ㎟ 27 27 ASTM D-882 ELONGATION AT BREAK MD TD % % 160 140 ASTM D-882 F - 5 VALUE MD TD kg / ㎟ kg / ㎟ 11.0 11.0 ASTM D-882 HEAT-SHRINKAGE (10min, 200℃) MD TD % % 5.0 0.0 ASTM D-2305 FRICTION COEFFICIENT uS uK   0.35 0.45 ASTM D-1894 WETTING TENSION IN OUT dyne/cm dyne/cm 52 40 ASTM D-2578 HAZE FF   % FF 2.5 DK ASTM D-1003 TEST CONTDITION Normal laboratory condition : 23℃, 50%RH

FP01 25MIC

PROPERTY METRIC(S.I.)UNITS TEST METHOD UNIT TYPICAL VALUE AVERAGE THICKNESS ㎛ 25   YIELD m²/ kg 28.6   TENSILE STRENGTH MD TD kg / ㎟ kg / ㎟ 30 23 ASTM D-882 ELONGATION AT BREAK MD TD % % 160 140 ASTM D-882 F - 5 VALUE MD TD kg / ㎟ kg / ㎟ 13 11 ASTM D-882 HEAT-SHRINKAGE (10min, 200℃) MD TD % % 5.0 0.2 ASTM D-2305 FRICTION COEFFICIENT uS uK   0.27 0.35 ASTM D-1894 WETTING TENSION IN OUT dyne/cm dyne/cm 52 40 ASTM D-2578 HAZE FF   % FF 1.2 DK ASTM D-1003 TEST CONTDITION Normal laboratory condition : 23℃, 50%RH

FP01 38MIC

PROPERTY METRIC(S.I.)UNITS TEST METHOD UNIT TYPICAL VALUE AVERAGE THICKNESS ㎛ 38   YIELD m²/ kg 18.8   TENSILE STRENGTH MD TD kg / ㎟ kg / ㎟ 27 21 ASTM D-882 ELONGATION AT BREAK MD TD % % 145 145 ASTM D-882 F - 5 VALUE MD TD kg / ㎟ kg / ㎟ 13 11 ASTM D-882 HEAT-SHRINKAGE (10min, 200℃) MD TD % % 4.0 0.2 ASTM D-2305 FRICTION COEFFICIENT uS uK   0.20 0.27 ASTM D-1894 WETTING TENSION IN OUT dyne/cm dyne/cm 52 40 ASTM D-2578 HAZE FF   % FF 1.6 DK ASTM D-1003 TEST CONTDITION Normal laboratory condition : 23℃, 50%RH